Sheldrickite

Sheldrickite is a sodium calcium carbonate fluoride mineral, named in honor of George M. Sheldrick, former Professor of Crystallography at the University of Göttingen in Germany.[2] Sheldrick is the creator of SHELLX computer program widely used for the analysis of crystal structures.[2] Determination of the structure of this mineral required the software's capability of handling twinned crystals.[2]

Sheldrickite
General
Category	carbonates
Formula (repeating unit)	NaCa3 (CO3) 2 F3 •(H2O)
Strunz classification	V/C.06-27
Dana classification	16a.3.11.1
Crystal system	Trigonal
Unit cell	a = 6.726 Å; c = 15.05 Å; Z = 3
Identification
Formula mass	338.25 gm
Color	colorless to white
Crystal habit	Aggregates of blocky twinned crystals, radiating thin flakes and fibrous masses to 2mm.
Twinning	By reflection on {001}
Cleavage	parting on [001] good
Fracture	uneven
Tenacity	Brittle
Mohs scale hardness	3
Luster	vitreous to silky
Streak	white
Specific gravity	2.86
Density	2.86 g/cm^3
Optical properties	Semitransparent
References	[1][2][3]

Occurrence

Sheldrickite is a rare mineral found in Mont Saint-Hilaire, Canada.[1] Mont Saint-Hilaire is an alkaline intrusive complex and one of the ten Monteregian Hills.[1] A series of plutons is aligned along the St. Lawrence Valley for almost 150 km eastward from Oka to Megantic. Sheldrickite is closely associated with shortite (Na₂Ca₂(CO₃)), with the crystals being found in a cavity between shortite crystals.[1] Sheldrickite also occurs as flakes in thin seams between crystals of shortite.[1] Sheldrickite is thought to be formed in a late-stage hydrothermal infilling.[1] The associated species of Sheldrickite include pectolite, microcline, arfvedsonite, aegirine, polylithionite, calcite, fluorite and minor molybdenite, leucosphenite, thenardite, thermonatrite, sphalerite, galena, schairerite and kogarkoite.[1]

Physical and Optical Properties

Sheldrickite has 2 distinct habits,one occurs as a 1x1x2 mm aggregate of blocky twined crystals with 0.1x0.1x0.1 mm individuals.[1] The second habit occurs as a radiating thin white silky flakes to fibrous masses up to 2 mm wide.[1] Each habit was established as the same species by X-ray diffraction, infrared spectroscopy, and electron-microprobe data. This mineral is colorless to white, it has a white streak and a vitreous luster.[1] It has a brittle uneven fracture and has good {001} parting.[1] It has no fluorescence and has a Mohs hardness of 3, and a density of 2.86 +-0.04 g/cm².[1]

Crystallography

Sheldrickite is Trigonal-pyramidal with the space group being P3₂. This mineral has an axial ratio of 1:2.24025, with cell dimensions of a = 6.718 Å, c = 15.05 Å, Z = 3 Å; V = 588.23 Å.[3] The precession photographs show sheldrickite to be hexagonal with a diffraction symmetry of 6/mmm, with space-group choices P6₂22 and P6₄22.[1] After the solution of the crystal structure, it was shown that the actual symmetry of sheldrickite is trigonal, space group P3₂ and the pseudohexagonal symmetry is due to merohedral twinning.[1]

Chemical Composition

Oxide	wt%	Range
Na2O	6.80	6.80-9.16
CaO	35.55	35.55-49.74
H2O	.6	.6-5.33
CO2	7.10	7.10-26.02
Oxygen	33.11	-
Fluorine	16.85	-
Total	100	100

[3]

Structure

The structure of sheldrickite has four large-cation sites, but only two distinct types of polyhedral.[1] The Sodium (Na) polyhedron, with its 8-fold coordination, fits the compressed octahedron that is modified by the removal of one edge.[1] The compressed axis corresponds to the Na-F bonds, where the removed edge results in the four longer bonds in the polyhedron.[1] Each of these three Calcium (Ca) sites has a similar stereochemistry and a similar polyhedron, in the nine-fold coordination.[1] The polyhedron fits within the irregular trigonal prism, with the three Fluorine (F) atoms defining the equatorial plane and the other six ligands and the upper and lower face of the prism.[1] The crystal structure of sheldrickite is layered on (001).[1] In sheldrickite, there are two layers of different composition: (1) Na(CO₃)₂*H₂O, and (2) CaF. The pseudo-m planes are positioned through the Na(CO₃)₂*H₂O layers, and the pseudo-2-fold axis along [100] is at 0,0,0.[1] The carbonate layer is the mixed-layer type and the standing on end (CO₃) groups are not in a separate layer but occur with the cations and H₂O groups.[1] Sheldrickite structure is a combination of the bastnäsite - (Ce) structure with segregated large-cation layers and (CO₃) layers, and the cebaite - (Ce) structure with integrated large-cation and (CO₃) groups in the same layer.[1] Sheldrickite has a segregated large-cation layer and an integrated large cation - (H₂O) - (CO₃) layer.[1]

References

1. Grice, J.D., et. al., 1997, Sheldrickite, a new sodium-calcium-fluorocarbonate mineral species from Mont Saint-Hilaire, Quebec: The Canadian Mineralogist, Vol. 35, pp. 181-187, http://rruff.info/doclib/cm/vol35/CM35_181.pdf
2. https://www.mindat.org/min-7289.html
3. http://webmineral.com/data/Sheldrickite.shtml#.Wia_JTdryUk